Ultramid B3WG6 BK00564
PA6-GF30BASF67056 Ludwigshafen, Germany Glass fibre reinforced and heat ageing resistant injection moulding grade used e.g. for automobile manifolds and pedals. The products can also be offered as BMBcert™ and/or Ccycled™. Due to the Massbalance approach the product properties do not change.
물성치 데이터
Typical values for uncoloured product at 23°C
| 물성 항목 | 시험 방법 | 단위 | 건조 (Dry) | 조습 (Cond.) |
|---|---|---|---|---|
| properties | ||||
| Polymer abbreviation | - | - | PA6-GF30 | |
| Density | ISO 1183 | kg/m³ | 1360 | |
| Viscosity number (0.5% in 96% H2 SO4 ) | ISO 307, 1157, 1628 | cm³/g | 145 | |
| Water absorption, saturation in water at 23°C | similar to ISO 62 | % | 6.3 - 6.9 | |
| Moisture absorption, equilibrium 23°C/50% r.h. | similar to ISO 62 | % | 1.9 - 2.3 | |
| processing | ||||
| Melting temperature, DSC | ISO 11357-1/-3 | °C | 220 | |
| MVR 275 °C/5 kg | ISO 1133 | cm³/10min | 35 | |
| Melt temperature, injection moulding/extrusion | - | °C | 270 - 290 | |
| Mould temperature, injection moulding | - | °C | 80 - 90 | |
| Moulding shrinkage, constrained | - | % | 0.3 | |
| Molding shrinkage (parallel) | ISO 294-4 | % | 0.30 | |
| Molding shrinkage (normal) | ISO 294-4 | % | 0.85 | |
| Pre/Post-processing, Pre-drying, Temperature | - | °C | 80 | |
| Pre/Post-processing, Pre-drying, Time | - | h | 4 | |
| Melt temperature | - | °C | 280 | |
| Mold temperature | - | °C | 80 | |
| flammability | ||||
| UL94 flammability rating at nominal 1.5 mm (thickness tested) | IEC 60695-11-10 | class (mm) HB (1.47) | ||
| Yellow Card available | - | - | yes | |
| UL94 flammability rating (thickness tested) | IEC 60695-11-10 | class (mm) HB (0.75) | ||
| Automotive materials (Thickness >= 1 mm) | ISO 3795, FMVSS 302 | - | + | |
| Glow Wire Ignition Temperature, GWIT ( | IEC 60695-2-13 | °C | 675 | |
| Thickness GWIT ( | IEC 60695-2-13 | mm | 1 | |
| mechanical | ||||
| Tensile modulus | ISO 527-1/-2 | MPa | 9600 | 5700 |
| Stress at break | ISO 527-1/-2 | MPa | 170 | 100 |
| Strain at break | ISO 527-1/-2 | % | 3.3 | 7 |
| Flexural modulus | ISO 178 | MPa | 9000 | 5300 |
| Flexural strength | ISO 178 | MPa | 260 | 160 |
| Charpy unnotched impact strength (23°C) | ISO 179/1eU | kJ/m² | 80 | 90 |
| Charpy unnotched impact strength (-30°C) | ISO 179/1eU | kJ/m² | 65 | 70 |
| Charpy notched impact strength (23°C) | ISO 179/1eA | kJ/m² | 10 | 18 |
| Charpy notched impact strength (-30°C) | ISO 179/1eA | kJ/m² | 8 | 8 |
| Izod impact strength (23°C) | ISO 180/U | kJ/m² | 70 | - |
| Tensile modulus 80°C | ISO 527-1/-2 | MPa | 4500 | - |
| Stress at break 80°C | ISO 527-1/-2 | MPa | 95 | - |
| Strain at break 80°C | ISO 527-1/-2 | % | 8 | - |
| thermal | ||||
| Deflection temp. under load 1.8 MPa (HDT A) | ISO 75-1/-2 | °C | 205 | |
| Deflection temp. under load 0.45 MPa (HDT B) | ISO 75-1/-2 | °C | 220 | |
| Max. service temperature (short cycle operation) | - | °C | 200 | |
| Temperature index at 50% loss of tensile strength after 5000 h | IEC 60216 | °C | 175 | |
| Temperature index at 50% loss of tensile strength after 20000 h | IEC 60216 | °C | 145 | |
| Coefficient of linear thermal expansion, longitudinal (23-55)°C | ISO 11359-1/-2 | E-6/K | 25 | |
| Coefficient of linear thermal expansion, transverse (23-55)°C | ISO 11359-1/-2 | E-6/K | 102 | |
| electrical | ||||
| Comparative tracking index, CTI, test liquid A | IEC 60112 | - | - | 400 |
기술 자료
관련 PA6-GF30 Grade
Glass fibre reinforced and heat aging resistant injection moulding grade, e.g.used for automobile parts with high stiffness requirements under the hood. The products can also be offered as BMBcert™ and/or Ccycled™. Due to the Massbalance approach the product properties do not change.
Deep Gloss D3K R01 BK23361 03/2026 PA Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 Ultramid® Deep Gloss D3K R01 BK23361 is an easy-flowing, UV-stabilized polyamide for injection molding. This grade has excellent surface appearance for high-gloss applications and was designed to offer high level scratch and mar resistance.
D3WG12 Aqua BK00102 03/2026 PA-GF60 BASF Corporation Ultramid® D3WG12 Aqua BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid® D3WG12 Aqua BK00102 shows improved retention of
D3EG12 Aqua BK00102 03/2026 PA-GF60 BASF Corporation
B3ZG8 HB BK23309 03/2026 PA6-I GF40 Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 B3ZG8 HB BK23309 is 40% glass fiber reinforced and impact modified PA6 grade for injection molding and high impact applications.
B3ZG7 OSI BK23273 10/2023 PA6-I-GF35 BASF Corporation Ultramid® B3ZG7 OSI BK2373 is a 35% glass reinforced, pigmented black, heat stabilized, impact modified Polyamide 6 injection molding grade. It was developed to meet demanding mechanical and chemical requirements for the automotive oil pan application.