Ultramid B3UG4
PA6BASF67056 Ludwigshafen, Germany Without halogens and posphorous flame retardant glass fiber reinforced injection moulding grade with outstanding flowability properties, good electrical properties and low smoke density. The product is resistant to the glow wire test GWFI up to 960 °C. Due to the halide free stabilization the impact on corrosion is minimized and sensitive electronic components are better protected.
물성치 데이터
Typical values for uncoloured product at 23°C
| 물성 항목 | 시험 방법 | 단위 | 건조 (Dry) | 조습 (Cond.) |
|---|---|---|---|---|
| properties | ||||
| Polymer abbreviation | - | - | PA6-GF20 FR(30) | |
| Density | ISO 1183 | kg/m³ | 1310 | |
| Viscosity number (0.5% in 96% H2 SO4 ) | ISO 307, 1157, 1628 | cm³/g | 150 | |
| Water absorption, saturation in water at 23°C | similar to ISO 62 | % | 6.6 - 7.2 | |
| Moisture absorption, equilibrium 23°C/50% r.h. | similar to ISO 62 | % | 2 - 2.4 | |
| processing | ||||
| Melting temperature, DSC | ISO 11357-1/-3 | °C | 220 | |
| MVR 275 °C/5 kg | ISO 1133 | cm³/10min | 80 | |
| Melt temperature, injection moulding/extrusion | - | °C | 250 - 275 | |
| Mould temperature, injection moulding | - | °C | 80 - 90 | |
| Molding shrinkage, model-housing 1.5 mm | - | % | 0.5 | |
| Molding shrinkage (parallel) | ISO 294-4 | % | 0.80 | |
| Molding shrinkage (normal) | ISO 294-4 | % | 0.80 | |
| thermal | ||||
| Deflection temp. under load 1.8 MPa (HDT A) | ISO 75-1/-2 | °C | 170 | |
| Deflection temp. under load 0.45 MPa (HDT B) | ISO 75-1/-2 | °C | 210 | |
| tensile strength | IEC 60216 | °C | 160 | |
| Coeff. of linear therm. expansion 23°C - 55°C (parallel) | ISO 11359-1/-2 | E-6/K | 41 | |
| Coeff. of linear therm. expansion 23°C - 55°C (normal) | ISO 11359-1/-2 | E-6/K | 86 | |
| flammability | ||||
| GWFI (thickness) | IEC 60695-2-12 | °C (mm) 960 (1) | ||
| Railway: Hazard level acc. to requ. sets R22 and R23 EN 45545-2 class HL2 (1 | - | 3mm) | ||
| electrical | ||||
| Relative permittivity (1 MHz) | IEC 62631-2-1 | - | 3.8 | - |
| Dissipation factor (1 MHz) | IEC 62631-2-1 | E-4 | 150 | - |
| Volume resistivity | IEC 62631-3-1 | Ohm*m | 1E13 | 1E9 |
| Surface resistivity | IEC 62631-3-2 | Ohm - / | 1E12 | |
| CTI, solution A | IEC 60112 | - | 550 | |
| Electric strength K20/K20, (60*60*1 mm³) | IEC 60243-1 | kV/mm | 35 | 34 |
| mechanical | ||||
| Tensile modulus | ISO 527-1/-2 | MPa | 6000 | 3000 |
| Stress at break | ISO 527-1/-2 | MPa | 90 | 50 |
| Strain at break | ISO 527-1/-2 | % | 3 | 20 |
| Flexural modulus | ISO 178 | MPa | 5700 | 2800 |
| Flexural strength | ISO 178 | MPa | 150 | 70 |
| Charpy unnotched impact strength, 23°C | ISO 179/1eU | kJ/m² | 40 | 110 |
| Charpy unnotched impact strength, -30°C | ISO 179/1eU | kJ/m² | 35 | - |
| Charpy notched impact strength, 23°C | ISO 179/1eA | kJ/m² | 3 | 9 |
| Charpy notched impact strength, -30°C | ISO 179/1eA | kJ/m² | 3.4 | - |
기술 자료
관련 PA6 Grade
Glass fibre reinforced and heat aging resistant injection moulding grade, e.g.used for automobile parts with high stiffness requirements under the hood. The products can also be offered as BMBcert™ and/or Ccycled™. Due to the Massbalance approach the product properties do not change.
Deep Gloss D3K R01 BK23361 03/2026 PA Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 Ultramid® Deep Gloss D3K R01 BK23361 is an easy-flowing, UV-stabilized polyamide for injection molding. This grade has excellent surface appearance for high-gloss applications and was designed to offer high level scratch and mar resistance.
D3WG12 Aqua BK00102 03/2026 PA-GF60 BASF Corporation Ultramid® D3WG12 Aqua BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid® D3WG12 Aqua BK00102 shows improved retention of
D3EG12 Aqua BK00102 03/2026 PA-GF60 BASF Corporation
B3ZG8 HB BK23309 03/2026 PA6-I GF40 Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 B3ZG8 HB BK23309 is 40% glass fiber reinforced and impact modified PA6 grade for injection molding and high impact applications.
B3ZG7 OSI BK23273 10/2023 PA6-I-GF35 BASF Corporation Ultramid® B3ZG7 OSI BK2373 is a 35% glass reinforced, pigmented black, heat stabilized, impact modified Polyamide 6 injection molding grade. It was developed to meet demanding mechanical and chemical requirements for the automotive oil pan application.