Ultramid B3GK35 BK23238
PA6BASFB3GK35 BK23238 03/2026 PA6+(GF+GB)40% Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 A combined glass-fibre and glass-bead reinforced injection moulding grade for industrial articles having very high dimensional stability, used e.g. for automobile exteriors and housings for electronics.
물성치 데이터
Typical values for uncoloured product at 23°C
| 물성 항목 | 시험 방법 | 단위 | 건조 (Dry) | 조습 (Cond.) |
|---|---|---|---|---|
| properties | ||||
| Polymer abbreviation | - | - | PA6+(GF+GB)40% | |
| Density | ISO 1183 | kg/m³ | 1440 | |
| Viscosity number (0.5% in 96% H2 SO4 ) | ISO 307, 1157, 1628 | cm³/g | 126 | |
| processing | ||||
| Melting temperature, DSC | ISO 11357-1/-3 | °C | 220 | |
| mechanical | ||||
| Tensile modulus | ISO 527-1/-2 | MPa | 8100 | 4300 |
| Stress at break | ISO 527-1/-2 | MPa | 135 | 75 |
| Strain at break | ISO 527-1/-2 | % | 3.2 | 7.5 |
| Flexural modulus | ISO 178 | MPa | 7200 | 4100 |
| Flexural strength | ISO 178 | MPa | 205 | 125 |
| Charpy notched impact strength (23°C) | ISO 179/1eA | kJ/m² | 7 | 14 |
| Izod notched impact strength (23°C) | ISO 180/A | kJ/m² | 7 | 14 |
| Izod notched impact strength (-30°C) | ISO 180/A | kJ/m² | 5 | 6 |
| thermal | ||||
| Deflection temp. under load 1.8 MPa (HDT A) | ISO 75-1/-2 | °C | 197 | |
기술 자료
관련 PA6 Grade
Glass fibre reinforced and heat aging resistant injection moulding grade, e.g.used for automobile parts with high stiffness requirements under the hood. The products can also be offered as BMBcert™ and/or Ccycled™. Due to the Massbalance approach the product properties do not change.
Deep Gloss D3K R01 BK23361 03/2026 PA Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 Ultramid® Deep Gloss D3K R01 BK23361 is an easy-flowing, UV-stabilized polyamide for injection molding. This grade has excellent surface appearance for high-gloss applications and was designed to offer high level scratch and mar resistance.
D3WG12 Aqua BK00102 03/2026 PA-GF60 BASF Corporation Ultramid® D3WG12 Aqua BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid® D3WG12 Aqua BK00102 shows improved retention of
D3EG12 Aqua BK00102 03/2026 PA-GF60 BASF Corporation
B3ZG8 HB BK23309 03/2026 PA6-I GF40 Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 B3ZG8 HB BK23309 is 40% glass fiber reinforced and impact modified PA6 grade for injection molding and high impact applications.
B3ZG7 OSI BK23273 10/2023 PA6-I-GF35 BASF Corporation Ultramid® B3ZG7 OSI BK2373 is a 35% glass reinforced, pigmented black, heat stabilized, impact modified Polyamide 6 injection molding grade. It was developed to meet demanding mechanical and chemical requirements for the automotive oil pan application.