A3WG10

Name: A3WG10
Brand: BASF

PA66-GF50BASF

Ultramid® A3WG10는 유리섬유 50% 강화 PA66 고강성 등급입니다. 금속 대체가 가능한 수준의 강성과 강도를 제공하며, 구조용 브래킷, 프론트엔드 캐리어 등에 사용됩니다.

물성치 데이터

Typical values for uncoloured product at 23°C

물성 항목	시험 방법	단위	건조 (Dry)	조습 (Cond.)
properties
Polymer abbreviation	-	-	PA66-GF50
Density	ISO 1183	kg/m³	1560
Viscosity number (0.5% in 96% H2 SO4 )	ISO 307, 1157, 1628	cm³/g	130
Moisture absorption, equilibrium 23°C/50% r.h.	similar to ISO 62	%	1 - 1.4
Water absorption, saturation in water at 23°C	similar to ISO 62	%	3.7 - 4.3
processing
Melting temperature, DSC	ISO 11357-1/-3	°C	260
MVR 275 °C/5 kg	ISO 1133	cm³/10min	10
Melt temperature, injection moulding/extrusion	-	°C	290 - 310
Mould temperature, injection moulding	-	°C	80 - 100
Moulding shrinkage, constrained	-	%	0.42
Molding shrinkage (parallel)	ISO 294-4	%	0.35
Molding shrinkage (normal)	ISO 294-4	%	0.95
injection molding, Melt temperature, recommended	-	°C	300
injection molding, Mold temperature, recommended	-	°C	100
Pre/Post-processing, Pre-drying, Temperature	-	°C	80
Pre/Post-processing, Pre-drying, Time	-	h	4
flammability
UL94 flammability rating at nominal 1.5 mm (thickness tested)	IEC 60695-11-10		class (mm) HB (1.54)
Yellow Card available	-	-	yes
UL94 flammability rating (thickness tested)	IEC 60695-11-10		class (mm) HB (0.8)
Automotive materials (Thickness ≥ 1 mm)	ISO 3795, FMVSS 302	-	+
Oxygen index	ISO 4589-1/-2	%	24
mechanical
Tensile modulus	ISO 527-1/-2	MPa	16800	12500
Stress at break	ISO 527-1/-2	MPa	240	180
Strain at break	ISO 527-1/-2	%	2.5	3.5
Tensile creep modulus, 1000 h, strain ≤ 0.5%, 23°C	ISO 899-1	MPa	*	7800
Flexural modulus	ISO 178	MPa	15000	13500
Flexural strength	ISO 178	MPa	360	300
Charpy unnotched impact strength (23°C)	ISO 179/1eU	kJ/m²	95	100
Charpy unnotched impact strength (-30°C)	ISO 179/1eU	kJ/m²	90	103
Charpy notched impact strength (23°C)	ISO 179/1eA	kJ/m²	18	25
Charpy notched impact strength (-30°C)	ISO 179/1eA	kJ/m²	13	12.6
Izod notched impact strength (23°C)	ISO 180/A	kJ/m²	13	14.5
thermal
Deflection temp. under load 1.8 MPa (HDT A)	ISO 75-1/-2	°C	250
Deflection temp. under load 0.45 MPa (HDT B)	ISO 75-1/-2	°C	250
Max. service temperature (short cycle operation)	-	°C	240
Temperature index at 50% loss of tensile strength after 5000 h	IEC 60216	°C	175
Temperature index at 50% loss of tensile strength after 20000 h	IEC 60216	°C	145
Coefficient of linear thermal expansion, longitudinal (23-55)°C	ISO 11359-1/-2	E-6/K	16
Coefficient of linear thermal expansion, transverse (23-55)°C	ISO 11359-1/-2	E-6/K	80
Thermal conductivity	DIN 52612-1	W/(m K)	0.37
Specific heat capacity	-	J/(kg*K)	1300